Feature
A Matting Agent for PVC PU leather coating is a substance that is added to the coating formulation to create a matte
or satin finish on the leather surface. It helps to reduce the glossiness of the coating and provide a more natural and
textured appearance.
There are several types of matting agents that can be used for PVC PU leather coating, including:
1. Silica Matting Agents: Silica particles are commonly used as matting agents in coatings. They are available in various
particle sizes and can be added to the coating formulation to create different levels of matting effect.
2. Polyethylene Wax: Polyethylene wax is another commonly used matting agent for PVC PU leather coating. It is available
in different grades and can be added to the coating formulation to provide a matte or satin finish.
3. Acrylic Matting Agents: Acrylic matting agents are synthetic polymers that can be added to the coating formulation to
create a matte or satin finish. They are available in both powder and liquid form.
4. Organic Matting Agents: Organic matting agents, such as amorphous silica or polymeric beads, can also be used for
PVC PU leather coating. These agents provide a soft and velvety appearance to the leather surface.
The selection of the matting agent depends on the desired level of matting effect, the type of leather, and the specific
requirements of the coating application. It is recommended to consult with a coating specialist or supplier to determine
the most suitable matting agent for a specific PVC PU leather coating formulation.
Black leather paint material is typically made from a combination of pigments, binders, and solvents. Pure Silica Powder
is not typically used in leather paint materials. Silica powder is commonly used in various industries for its abrasive,
absorbent, and anti-caking properties. It is not a common ingredient in leather paint formulations.
USING TIPS:
* Recommend dosage is 3%-8%. (Please adjust the dosage according to the actual product.) * As different formulations and conditions, suggest the user to test and make sure the dosage before using. | Item | SS-318 | Brand | SKYSIL |
| Content of SiO2,(dry basis) %≥ | ≥ 99 | Whiteness | ≥ 90 |
| Porosity ml/g | 1.3-1.4 | Particle Size(Malvent),um | 3.0-3.5 |
| Loss on drying (105℃,2Hrs),% | ≤5.0 | PH | 6.0-7.0 |
| Ignition Loss(1000℃,2Hrs),% | ≤6.0 | Oil Absorption g/100g | 260-320 |