Main features:
● Water dispersal type,emulsion form hydroxide Acrylic Resin
● High solid content,low viscosity,low acid value
● Mixed with dissociate cross-linking agent to be two component PU,has high gloss,high hardness
● Suitable for two component PU self-drying top coating and amino-baking top coatings
● Hydroxide Value:78-108mgKOH/g
Product Technical Index:
Appearance:milky white emulsion(Visual Observation)
Non-Volatile Matter:42±2.0%(120℃/30min)
PH value:7-8
Hydroxyl Value:78mgKOH/g(for solid resin,theoretical value)
Viscosity≤1000mPa.s(Rotational Viscometer)
Product Properties
This hydroxide acrylic dispersion can be diluted with water to construction viscosity. Its viscosity changes as PH value
changes.It can be mixed with poly aliphatic dissociate curing agent for preparing high–gloss top coating which can dry
fast at room temperature or dry by force at 80℃.
The film after curing has high gloss,hardness,limit film thickness and good water resistance.
This product has excellent pigment wetting and shear stability,can be grinned with dispersion directly.
Anticorrosion Pigments, Inkjet Receptive Coating, Matting Agent